To analyze the root cause of the great difference between the synthetic slag (slag prepared by chemical reagent) and premelted slag (molten slag in enterprise smelting) for physicochemical properties of PbO-Fe_xO-CaO-SiO₂-ZnO, the loss law of slag volatile for premelted slag and synthetic slag with the same composition with the 61.3% PbO are determined by FactSage and thermogravimetry, further, the volatile mechanism of lead slag is analyzed through combinate XRD and SEM-EDS analyze the final slag. The results shown that the volatilization of synthetic slag is more severe than that of premelted slag, synthetic lead slag had volatilized 12.7% before melting, and the main phase is Spinel of high melting point after volatilizing. But leads in premelted slag exists in the silicate is limited by the three-dimensional diffusion of silicate, which lead to a small amount of volatilization reaching the melting temperature. The mechanism function of weight loss process at high temperature of premelted slag and synthetic slag respectively are controlled by three-dimensional diffusion spherical symmetry Jander equation and Z-L-T equation, and the average apparent activation energies are 478.6kJ·mol^-1 and 352.9kJ·mol^-1.